Tailoring the chemical heterogeneity of Mn-modified 0.75BiFeO₃-0.25BaTiO₃ ceramics for piezoelectric sensor applications

The Mn-modified 0.75BiFeO₃-0.25BaTiO₃ (75BFBTMn) piezoelectric ceramic possesses a high depolarization temperature of 500 °C and a large piezoelectric coefficient of 110 pC/N, showing the potential for high temperature piezoelectric sensors. However, 75BFBTMn ceramic usually suffers dielectric degradation and abrupt drop of piezoelectric coefficient in the range of 300 °C to 500 °C. Combined the high-energy synchrotron X-ray diffraction analysis with Backscatter-SEM results, it is demonstrated that the electrical thermal instability is owing to the existence of chemical inhomogeneity. The Air-annealing treatment is able to decrease the volume fraction of pseudo-cubic phase and the lattice distortion, removes the chemical inhomogeneity in the grain and free Bi₂O₃ at grain boundary, and then eliminates dielectric anomalies and piezoelectric degradation with temperature. These results indicate that air-annealing is a simple but effective method to eliminate the chemical inhomogeneity in 75BFBTMn ceramics, thereby improving the property thermal stability for high temperature piezoelectric sensor applications. © 2022 Elsevier Ltd