Surface modification of ZnO nanocrystals

Nano-crystalline ZnO particles were synthesized using alcoholic solutions of zinc acetate dihydrate through a colloidal process. Five types of capping agents: 3-aminopropyl trimethoxysilane (Am), tetraethyl orthosilicate (TEOS), mercaptosuccinic acid (Ms), 3-mercaptopropyl trimethoxysilane (Mp) and polyvinylpyrrolidone (Pv) were added at the first ZnO precipitation time (first PPT) to limit the particle growth. The first three capping agents effectively capped the ZnO nanoparticles and limited the growth of the particles, while the last two capping agents caused agglomeration or larger clusters in the solutions. Particles synthesized were in the size range of 10-30 nm after capping, and grew to 60 and 100 nm in 3 and 6 weeks, respectively, during storage at ambient conditions. Refluxing time was found to only affect the first PPT time. Washing by ethanol and slow drying were very important in converting Zn(OH) ₂ into ZnO. XRD analyses revealed single phase ZnO Wurtzite crystal structure. Photoluminescence (PL) spectra showed high-intensity in UV emission and very low intensity in the visible emission, which indicates a good surface morphology of the ZnO nanoparticles with little surface defects. Optical absorption spectra showed a blue shift by the capped ZnO due to the quantum confinement effect by the single crystal size of 5-6 nm as analysed by TEM. Capping effectiveness of each agent is discussed through possible capping mechanism and chemical reaction of each capping agent. This synthesis process is a low cost, high purity, easy to control method using only bio-compatible materials. © 2007 Elsevier B.V. All rights reserved.