Surface gradient CoCrMo alloy generated by carbon ion implantation with enhanced tribocorrosion resistance

Research output: Journal Publications and Reviews (RGC: 21, 22, 62)21_Publication in refereed journal

4 Scopus Citations
View graph of relations

Author(s)

Detail(s)

Original languageEnglish
Pages (from-to)590-594
Journal / PublicationSurface and Coatings Technology
Volume320
Publication statusPublished - 25 Jun 2017

Abstract

The CoCrMo alloy was ion implanted by carbon with implantation fluences from 1.0 × 1017 to 9.0 × 1017 ions/cm2. The nanostructure and phase transformation in CoCrMo alloy due to carbon ion implantation were investigated using high-resolution transmission electron microscopy (HRTEM). The tribocorrosion behavior was investigated by using a ball-on-disk reciprocating wear tester equipped with a three-electrode electrochemical cell. It is found that the carbon ion-implanted CoCrMo alloy is composed of an amorphous layer, a transition layer with mixed amorphous/nanocrystalline, and the base material. The stacking faults (SFs) and nano ε-martensite enriched region are formed underneath the transition layer at higher implantation fluence. The material loss due to tribocorrosion is decreased by one order of magnitude after carbon ion implantation. The enhanced tribocorrosion performance can be explained by the formation of amorphous layer and the nanocrystallization during carbon ion implantation.

Research Area(s)

  • Friction, Ion implantation, Nanocrystals, TEM, Tribocorrosion