Scratch adhesion and tribological behaviour of graded Cr/CrN/CrTiN coatings synthesized by closed-field unbalanced magnetron sputtering

Research output: Journal Publications and Reviews (RGC: 21, 22, 62)21_Publication in refereed journalNot applicablepeer-review

16 Scopus Citations
View graph of relations

Author(s)

  • Mohammad Sharear Kabir
  • Paul Munroe
  • Zhifeng Zhou
  • Zonghan Xie

Detail(s)

Original languageEnglish
Pages (from-to)163-175
Journal / PublicationWear
Volume380-381
Publication statusPublished - 15 Jun 2017

Abstract

The scratch adhesion and tribological behavior of graded Cr/CrN/CrTiN coatings deposited on tool steels by closed-field unbalanced magnetron sputtering (CFUBMS) by varying the Ti sputtering current (ITi) was investigated in detail. The hardness and modulus of these coatings were determined prior to scratch and wear testing using nanoindentation methods, which yielded increasing hardness, modulus, and H/E and H3/E2 ratios with increasing Ti content. Progressive loading scratch tests from 1 N to 150 N at a speed of 4 mm/min were carried out using a Rockwell diamond indenter at a loading rate of 100 N/min on a 6 mm linear track. The dry sliding wear tests with a pin-on-disc arrangement under various wear parameters (sliding velocity, sliding distance and normal load) were carried out to investigate the tribological response of these graded coatings. The scratch test yielded the highest critical loads, i.e. LC1=~141 N and LC2=~149 N and a high scratch crack propagation resistance parameter (CPRS)=~1074 for the coating with the lowest Ti content. The initial failure of the coatings was due to conformal cracking leading to significant plastic deformation before complete substrate exposure. The coatings also yielded wear rates of the order ~10–16 m3/N m with abrasive wear as the dominant wear mechanism. Both the scratch toughness and wear resistance of the coatings decrease with increasing Ti content. The decrease in scratch toughness, wear resistance and damage tolerance of these coatings can be attributed to increasing modulus of these coatings as the Ti content increases, implying that a modulus mismatch exists between coating and substrate.

Research Area(s)

  • Closed-field unbalanced magnetron sputtering (CFUBMS), Critical load, Graded coatings, Hardness, Modulus, Scratch adhesion characteristic, Tribological response

Citation Format(s)

Scratch adhesion and tribological behaviour of graded Cr/CrN/CrTiN coatings synthesized by closed-field unbalanced magnetron sputtering. / Kabir, Mohammad Sharear; Munroe, Paul; Zhou, Zhifeng; Xie, Zonghan.

In: Wear, Vol. 380-381, 15.06.2017, p. 163-175.