Cyclic Fatigue-Crack Growth and Fracture Properties in Ti₃SiC₂ Ceramics at Elevated Temperatures

The cyclic fatigue and fracture toughness behavior of reactive hot-pressed Ti₃SiC₂ ceramics was examined at temperatures from ambient to 1200°C with the objective of characterizing the high-temperature mechanisms controlling crack growth. Comparisons were made of two monolithic Ti₃SiC₂ materials with fine- (3-10 μm) and coarse-grained (70-300 μm) microstructures. Results indicate that fracture toughness values, derived from rising resistance-curve behavior, were significantly higher in the coarser-grained microstructure at both low and high temperatures; comparative behavior was seen under cyclic fatigue loading. In each microstructure, ΔK_th fatigue thresholds were found to be essentially unchanged between 25° and 1100°C; however, there was a sharp decrease in ΔK_th at 1200°C (above the plastic-to-brittle transition temperature), where significant high-temperature deformation and damage are first apparent. The substantially higher cyclic-crack growth resistance of the coarse-grained Ti₃SiC₂ microstructure was associated with extensive crack bridging behind the crack tip and a consequent tortuous crack path. The crack-tip shielding was found to result from both the bridging of entire grains and from deformation kinking and bridging of microlamellae within grains, the latter forming by delamination along the basal planes.