Phase-Selective Epitaxial Growth of Heterophase Nanostructures on Unconventional 2H-Pd Nanoparticles

Heterostructured, including heterophase, noble-metal nanomaterials have attracted much interest due to their promising applications in diverse fields. However, great challenges still remain in the rational synthesis of well-defined noble-metal heterophase nanostructures. Herein, we report the preparation of Pd nanoparticles with an unconventional hexagonal close-packed (2H type) phase, referred to as 2H-Pd nanoparticles, via a controlled phase transformation of amorphous Pd nanoparticles. Impressively, by using the 2H-Pd nanoparticles as seeds, Au nanomaterials with different crystal phases epitaxially grow on the specific exposed facets of the 2H-Pd, i.e., face-centered cubic (fcc) Au (fcc-Au) on the (002)h facets of 2H-Pd while 2H-Au on the other exposed facets, to achieve well-defined fcc-2H-fcc heterophase Pd@Au core-shell nanorods. Moreover, through such unique facet-directed crystal-phase-selective epitaxial growth, a series of unconventional fcc-2H-fcc heterophase core-shell nanostructures, including Pd@Ag, Pd@Pt, Pd@PtNi, and Pd@PtCo, have also been prepared. Impressively, the fcc-2H-fcc heterophase Pd@Au nanorods show excellent performance toward the electrochemical carbon dioxide reduction reaction (CO₂RR) for production of carbon monoxide with Faradaic efficiencies of over 90% in an exceptionally wide applied potential window from -0.9 to -0.4 V (versus the reversible hydrogen electrode), which is among the best reported CO₂RR catalysts in H-type electrochemical cells.