Nanocrystalline Y₂O₃-modified metal matrix composite coatings with improved resistance to thermocyclic oxidation and V₂O₅-induced type II hot corrosion

Incorporating reactive elements (RE) into turbine coatings is a well-established surface treatment. However, suboptimal RE concentrations can lead to compromised strength, heightened brittleness, and reduced adhesion. In contrast, RE oxides offer advantages of avoiding these detrimental effects, counteracting corrosion phenomena induced by V₂O₅ compounds and enhancing oxidation resistance. A notable challenge lies in optimizing RE oxide particle incorporation and understanding the influence of particles in coating microstructures. This study focuses on developing Ni–Al and Ni-Cr-Al type metal matrix composite (MMC) coatings on Inconel 617 (IN617), containing up to 11 vol% of Yttria (Y₂O₃) nanoparticles. Y₂O₃ nanoparticles and Ni were co-electrodeposited on IN617 followed by either pack aluminizing or a two-step chromizing and aluminizing process. An even distribution of Y₂O₃ nanoparticles was observed throughout the entire 100 μm coating thickness, leading to significant grain refinement in the sub-micron to nano range in both coating types. Y₂O₃-strengthened coatings were subjected to oxidation at 1100 °C and hot corrosion at 700 °C and were compared to their Y₂O₃-free counterparts. Present at grain boundaries, Y₂O₃ markedly enhanced the oxidation and corrosion resistance by reducing interdiffusion, improving the oxide scale adherence and binding V₂O₅, highlighting the potential of this method for advanced turbine blade coatings. © 2024 The Authors. Published by Elsevier B.V.