Abstract
Nanocrystalline α-Ni(OH) 2 was prepared by an ultrasonic precipitation/stirring method. Results of X-ray diffraction, transmission electron microscopy, infrared, and thermogravimetric measurements confirm that the sample obtained is α phase. Compared with the sample prepared without ultrasonic stirring, the crystal structure of the α phase sample has been changed from β phase. The crystalline size of the sample is about 20 nm, which is smaller than the sample produced without ultrasonic stirring (70 nm).
| Original language | English |
|---|---|
| Pages (from-to) | 45-46 |
| Journal | Journal of Nanoscience and Nanotechnology |
| Volume | 2 |
| Issue number | 1 |
| DOIs | |
| Publication status | Published - 2002 |
| Externally published | Yes |
Bibliographical note
Publication details (e.g. title, author(s), publication statuses and dates) are captured on an “AS IS” and “AS AVAILABLE” basis at the time of record harvesting from the data source. Suggestions for further amendments or supplementary information can be sent to [email protected].Research Keywords
- IR
- Nanocrystalline α-Ni(OH) 2
- TEM
- Thermal Properties
- Ultrasonic Method
- XRD
Fingerprint
Dive into the research topics of 'Nanocrystalline α-Ni(OH) 2 Prepared by Ultrasonic Precipitation'. Together they form a unique fingerprint.Cite this
- APA
- Author
- BIBTEX
- Harvard
- Standard
- RIS
- Vancouver