Morphology of interfacial reaction between lead-free solders and electroless Ni-P under bump metallization

Research output: Journal Publications and ReviewsRGC 21 - Publication in refereed journalpeer-review

190 Scopus Citations
View graph of relations

Author(s)

Detail(s)

Original languageEnglish
Pages (from-to)6359-6363
Journal / PublicationJournal of Applied Physics
Volume88
Issue number11
Publication statusPublished - Dec 2000
Externally publishedYes

Abstract

The morphology of interfacial reaction products between four lead-free solder alloys on electroless Ni-P was characterized. The four Pb-free solders were 99.3Sn0.7Cu, 95.5Sn3.8Ag0.7Cu, 96.5Sn3.5Ag, and 96Sn2Ag2Bi (in wt%) alloys. After reflow, the interfacial intermetallics in the first two solders that contain Cu (99.3Sn0.7Cu and 95.5Sn3.8Ag0.7Cu) had good adhesion with electroless Ni-P. However, the 96.5Sn3.5Ag and 96Sn2Ag2Bi alloys formed interfacial intermetallics with a needle shaped morphology that spalled off the surface of electroless Ni-P. This difference is attributed to the role of Cu in the solders (which modified the chemical potential of the interfacial intermetallics), the volume change that occurs during intermetallic formation, and the interfacial properties of the compound. In solid state aging experiments, the consumption of electroless Ni-P by intermetallic growth was not significant (approximately 1 μm) and all the intermetallics had good adhesion to the electroless Ni-P. The electroless Ni-P exhibited some damage at the outer edge of the bond pad due to stress imposed during solid state aging. Large Ag3Sn and Cu6Sn5 intermetallics were observed in the bulk of the solders (except for SnAgBi solder), and these intermetallics are discussed in terms of soldering reaction at the interface and phase equilibrium. © 2000 American Institute of Physics.

Bibliographic Note

Publication details (e.g. title, author(s), publication statuses and dates) are captured on an “AS IS” and “AS AVAILABLE” basis at the time of record harvesting from the data source. Suggestions for further amendments or supplementary information can be sent to [email protected].

Citation Format(s)

Morphology of interfacial reaction between lead-free solders and electroless Ni-P under bump metallization. / Jang, J. W.; Frear, D. R.; Lee, T. Y. et al.
In: Journal of Applied Physics, Vol. 88, No. 11, 12.2000, p. 6359-6363.

Research output: Journal Publications and ReviewsRGC 21 - Publication in refereed journalpeer-review