PY - 2015/9
Y1 - 2015/9
N2 - The low thermal stability of nanocrystalline metals severely limits their applications at high temperatures. In this study, we investigate the nanocrystalline stabilization mechanisms for Fe-14Cr alloys with 1, 2, and 4 at. pct Hf addition at 1173 K (900 °C). Microstructural characterizations using aberration-corrected scanning transmission electron microscopy and energy-dispersive X-ray spectroscopy reveal high density of HfO2 nanoparticles with sizes of ~4 nm dispersed throughout the ferritic matrix. This indicates that kinetic stabilization by HfO2 nanoparticle pinning is primarily responsible for the observed high thermal stability. In addition, some Hf and Cr segregation on grain boundaries is observed in the Fe-14Cr-4Hf, suggesting the existence of thermodynamic stabilization at high Hf content. Second-phase precipitations such as hafnium carbide, M23C6, and Fe-Cr-Hf intermetallic phase are also found in the Fe-14Cr-4Hf, but their large sizes and inter-spacing suggest that their contribution to stabilization is minimal.
AB - The low thermal stability of nanocrystalline metals severely limits their applications at high temperatures. In this study, we investigate the nanocrystalline stabilization mechanisms for Fe-14Cr alloys with 1, 2, and 4 at. pct Hf addition at 1173 K (900 °C). Microstructural characterizations using aberration-corrected scanning transmission electron microscopy and energy-dispersive X-ray spectroscopy reveal high density of HfO2 nanoparticles with sizes of ~4 nm dispersed throughout the ferritic matrix. This indicates that kinetic stabilization by HfO2 nanoparticle pinning is primarily responsible for the observed high thermal stability. In addition, some Hf and Cr segregation on grain boundaries is observed in the Fe-14Cr-4Hf, suggesting the existence of thermodynamic stabilization at high Hf content. Second-phase precipitations such as hafnium carbide, M23C6, and Fe-Cr-Hf intermetallic phase are also found in the Fe-14Cr-4Hf, but their large sizes and inter-spacing suggest that their contribution to stabilization is minimal.
UR - http://www.scopus.com/inward/record.url?scp=84938554871&partnerID=8YFLogxK
UR - https://www.scopus.com/record/pubmetrics.uri?eid=2-s2.0-84938554871&origin=recordpage
U2 - 10.1007/s11661-015-2985-2
DO - 10.1007/s11661-015-2985-2
M3 - RGC 21 - Publication in refereed journal
SN - 1073-5623
VL - 46
SP - 4394
EP - 4404
JO - Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
JF - Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
IS - 9
ER -