Flexural and Peel Properties of High Performance Magnesium/Carbon-Fiber/PEEK Laminated Composites

Research output: Journal Publications and Reviews (RGC: 21, 22, 62)21_Publication in refereed journalpeer-review

View graph of relations



Original languageEnglish
Pages (from-to)1153-1158
Journal / PublicationKey Engineering Materials
Online published15 Oct 2004
Publication statusPublished - 2004
Externally publishedYes


Title7th Asia-Pacific Symposium on Engineering Plasticity and Its Applications (AEPA2004)
LocationShanghai Jiaotong University
Period22 - 26 September 2004


Mg/Carbon-Fiber/PEEK laminated composites were successfully fabricated through simple hot pressing. The flexural and peel properties of this Mg based laminated composites are examined and analyzed. The flexural stress and modulus along the longitudinal direction are 960 MPa and 54.6 GPa, respectively, suggesting a sufficiently high resistance against bending deflection. The peel strength is around 5 N/mm, superior to that of the epoxy-resin-adhered Al/CFRP laminated composites.