Abstract
Mg/Carbon-Fiber/PEEK laminated composites were successfully fabricated through simple hot pressing. The flexural and peel properties of this Mg based laminated composites are examined and analyzed. The flexural stress and modulus along the longitudinal direction are 960 MPa and 54.6 GPa, respectively, suggesting a sufficiently high resistance against bending deflection. The peel strength is around 5 N/mm, superior to that of the epoxy-resin-adhered Al/CFRP laminated composites.
| Original language | English |
|---|---|
| Pages (from-to) | 1153-1158 |
| Journal | Key Engineering Materials |
| Volume | 274-276 |
| Online published | 15 Oct 2004 |
| DOIs | |
| Publication status | Published - 2004 |
| Externally published | Yes |
| Event | 7th Asia-Pacific Symposium on Engineering Plasticity and Its Applications (AEPA2004) - Shanghai Jiaotong University, Shanghai, China Duration: 22 Sept 2004 → 26 Sept 2004 |
Research Keywords
- Flexture test
- Hot pressing
- Mg/carbon-fiber/PEEK laminated composites
- Peel test
Fingerprint
Dive into the research topics of 'Flexural and Peel Properties of High Performance Magnesium/Carbon-Fiber/PEEK Laminated Composites'. Together they form a unique fingerprint.Cite this
- APA
- Author
- BIBTEX
- Harvard
- Standard
- RIS
- Vancouver