Effect of Ni content on the microstructure and mechanical behaviour of CrAlNiN coatings deposited by closed field unbalanced magnetron sputtering

Research output: Journal Publications and Reviews (RGC: 21, 22, 62)21_Publication in refereed journalNot applicablepeer-review

1 Scopus Citations
View graph of relations

Author(s)

  • Chuhan Sha
  • Paul Munroe
  • Zhifeng Zhou
  • Zonghan Xie

Detail(s)

Original languageEnglish
Pages (from-to)445-455
Journal / PublicationSurface and Coatings Technology
Volume357
Early online date22 Oct 2018
Publication statusPublished - 15 Jan 2019

Abstract

Ni incorporation is known to impose an intriguing influence on the composition, microstructure and mechanical properties of nitride-based coatings prepared by physical vapour deposition. This work examined the effect of varying Ni concentrations, controlled by NiCr alloy target current (INiCr), on the microstructures and properties of CrAlNiN coatings deposited on to M2 tool steel substrates. These coatings were deposited by closed field unbalanced magnetron sputtering (CFUMS). The composition and structure of the as-deposited coatings were investigated by XPS, XRD, FIB, and TEM. Residual stresses were determined using the XRD-sin2ψ method. Nanoindentation tests were performed to assess mechanical properties of the CrAlNiN outer layer. At relatively low INiCr values, below 3 A, the grains within CrAlNiN layer underwent refinement, yet maintained a columnar structure. At higher INiCr values, from 3 to 5 A, the columnar grains transitioned into more equiaxed grains. Hardness values of 25–28 GPa at low INiCr values were associated with the high residual compressive stress, solid solution hardening and grain refinement.

Research Area(s)

  • Chromium aluminium nickel nitride, Magnetron sputtering, Mechanical properties, Nickel content, Structural evolution

Citation Format(s)

Effect of Ni content on the microstructure and mechanical behaviour of CrAlNiN coatings deposited by closed field unbalanced magnetron sputtering. / Sha, Chuhan; Munroe, Paul; Zhou, Zhifeng; Xie, Zonghan.

In: Surface and Coatings Technology, Vol. 357, 15.01.2019, p. 445-455.

Research output: Journal Publications and Reviews (RGC: 21, 22, 62)21_Publication in refereed journalNot applicablepeer-review