Comparison in in-vitro evaluation of wollastonite and dicalcium silicate coatings

Research output: Journal Publications and Reviews (RGC: 21, 22, 62)21_Publication in refereed journalpeer-review

1 Scopus Citations
View graph of relations

Author(s)

Detail(s)

Original languageEnglish
Pages (from-to)359-362
Journal / PublicationKey Engineering Materials
Volume288-289
Publication statusPublished - 2005

Abstract

In-vitro evaluation of plasma sprayed wollastonite and dicalcium silicate coatings was carried out by SBF soaking test and osteoblasts seeding test. Apatite layers were formed on the surfaces of the two coatings indicative of the excellent bioactivity. The formation rate of apatite is higher on dicalcium silicate than on wollastonite. The cause is believed to be the presence of orthosilicate species in the dicalcium silicate coating promoting easier leaching by exchanging H3O+ ions from the solution with calcium ions concentrated in the orthosilicate positions. At the same time, loss of soluble silicon occurs, and it is supposed to enhance the repolymerization of the silica gel layer and provide the active sites for the nucleation of apatite. The outcome is that apatite forms faster on dicalcium silicate than on wollastonite. The data obtained from the osteoblasts seeding test indicate that the wollastonite and dicalcium silicate coatings promote the proliferation of osteoblasts and possess excellent biocompatibility.

Research Area(s)

  • Bioactivity, Dicalcium silicate, Plasma sprayed, Wollastonite

Citation Format(s)

Comparison in in-vitro evaluation of wollastonite and dicalcium silicate coatings. / Liu, Xuanyong; Ding, Chuanxian; Chu, Paul K.

In: Key Engineering Materials, Vol. 288-289, 2005, p. 359-362.

Research output: Journal Publications and Reviews (RGC: 21, 22, 62)21_Publication in refereed journalpeer-review