Comparative study of interfacial reactions of Sn-Ag-Cu and Sn-Ag solders on Cu pads during reflow soldering

The interfacial reaction in soldering is a crucial subject for the solder-joint integrity and reliability in electronic packaging technology. However, electronic industries are moving toward lead-free alloys because of environmental concerns. This drive has highlighted the fact that the industry has not yet arrived at a decision for lead-free solders. Among the lead-free alloys, Sn-3.5Ag and Sn-3.5Ag-0.5Cu are the two potential candidates. Here, detailed microstructural studies were carried out to compare the interfacial reaction of Sn-3.5Ag and Sn-3.5Ag-0.5Cu solder with a ball grid array (EGA) Cu substrate for different reflow times. The Cu dissolution from the substrate was observed for different soldering temperatures ranging from 230°C to 250°C, and the dissolution was found to increase with time and temperature. Dissolution of Cu in the Sn-3.5Ag solder is so fast that, at 240°C, 12 μm of the Cu substrate is fully consumed within 5 min. Much less dissolution is observed for the Sn-3.5Ag-0.5Cu solder. In respect to such high dissolution, there is no significant difference observed in the intermetallic compound (IMC) thickness at the interface for both solder alloys. A simplistic theoretical approach is carried out to find out the amount of Cu₆Sn₅ IMCs in the bulk of the solder by the measurement of the Cu consumption from the substrate and the thickness of the IMCs that form on the interface.