A novel polyurethane prepolymer as toughening agent : Preparation, characterization, and its influence on mechanical and flame retardant properties of phenolic foam

Research output: Journal Publications and Reviews (RGC: 21, 22, 62)21_Publication in refereed journalpeer-review

56 Scopus Citations
View graph of relations

Author(s)

  • Hongyu Yang
  • Xin Wang
  • Haixia Yuan
  • Lei Song
  • Yuan Hu
  • Guan Heng Yeoh

Detail(s)

Original languageEnglish
Pages (from-to)2720-2728
Journal / PublicationJournal of Applied Polymer Science
Volume128
Issue number5
Publication statusPublished - 5 Jun 2013

Abstract

A novel phosphorus- and silicon-containing polyurethane prepolymer (PSPUP) was synthesized by the chemical reaction of phenyl dichlorophosphate with hydroxy-terminated polydimethylsiloxane (HTPDMS) and subsequently with toluene-2,4-diisocyanate. The structure of PSPUP was confirmed by Fourier transform infrared spectroscopy and 1H nuclear magnetic resonance. Afterward, a series of phenolic foams (PF) with different loadings of PSPUP toughening agent were prepared. The apparent density and scanning electron microscopy results showed that the addition of PSPUP can increase the apparent density of phenolic foam. The compressive, impact and friability test results showed that the incorporation of PSPUP into PF dramatically improved the compressive strength, impact strength, and reduced the pulverization ratio, indicating the excellent toughening effect of PSPUP. The limiting oxygen index of PSPUP modified phenolic foams remained a high value and the UL-94 results showed all samples can pass V0 rating, indicating the modified foams still had good flame retardance. The thermal properties of the foams were investigated by thermogravimetric analysis under air atmosphere. Moreover, the thermal degradation behaviors of the PF and PSPUP/PF were investigated by real-time Fourier transform infrared spectra. © 2012 Wiley Periodicals, Inc.

Research Area(s)

  • flame retardance, foams, mechanical properties, thermal properties

Citation Format(s)

A novel polyurethane prepolymer as toughening agent : Preparation, characterization, and its influence on mechanical and flame retardant properties of phenolic foam. / Yang, Hongyu; Wang, Xin; Yu, Bin; Yuan, Haixia; Song, Lei; Hu, Yuan; Yuen, Richard K.K.; Yeoh, Guan Heng.

In: Journal of Applied Polymer Science, Vol. 128, No. 5, 05.06.2013, p. 2720-2728.

Research output: Journal Publications and Reviews (RGC: 21, 22, 62)21_Publication in refereed journalpeer-review